K.S. Guan
金属学报(英文版)
Atomic growth process and structure of Amorphous Electroless Coating have beenstudied, using Monte-Carlo simulation method. The simulation results of amorphousNi80P20 coating show that PDFs are in accordance with practical values. The mi-grations of adatoms in coating's growth are different from that of solidification ofamorphous materials. In some cases, the migrated adatoms in the process of growthof amorphous coating are not enough to occupy all vacancies and traps, so the amor-phous coating is micro-porous. The immovable probability k and the largest migrationdistance of adatoms, which lie on the electroless bath components, affect the PDF,volume density and microporosity remarkably.
关键词:
electroless Ni-P alloy
,
null
,
null
,
null
王敏
,
刘锦云
,
李文鹏
,
陈立甲
表面技术
doi:10.16490/j.cnki.issn.1001-3660.2015.06.004
目的：在锡青铜基体上化学镀Ni-P合金镀层,提高锡青铜的耐磨性和耐腐蚀性。方法以酸性含锌活化液活化锡青铜试样,在相同的条件下实施化学镀,并对镀态试样进行不同温度(250,400,500℃)下的热处理。对比基体、镀态试样和热处理试样的性能,研究热处理温度对锡青铜化学镀Ni-P合金层微观结构、显微硬度、耐磨性和耐腐蚀性的影响。结果锡青铜表面形成了Ni-P合金镀层,并且镀层无孔隙缺陷,与基体结合良好,沉积速率较快,为10.00μm/h。经热处理后,镀层的微观结构由非晶态向晶态转变,在500℃热处理的镀层显微硬度最大,耐磨性最好。镀态镀层和经250℃热处理的镀层在10%HNO3溶液和10%H2 SO4溶液(10%均为体积分数)中的耐腐蚀性明显好于锡青铜基体,镀态镀层在两种介质溶液中的腐蚀速率分别为0.225,0.146 mg/( cm2·d)。结论采用酸性含锌活化液活化锡青铜基体,可以在锡青铜表面制备出化学镀Ni-P合金镀层,且镀覆效果较好。这表明紫铜化学镀Ni-P合金工艺同样适用于锡青铜。
关键词:
锡青铜
,
酸性含锌活化液
,
化学镀Ni-P合金
,
耐磨性
,
耐腐蚀性
方信贤
腐蚀科学与防护技术
研究了硫酸铜加入量对化学镀Ni-Cu-P合金的镀层成分、组织及热稳定性影响,用中性盐雾实验和在20%H_2SO_4+20 g/LAl_2O_3溶液中的冲刷腐蚀实验研究了Ni-P与Ni-Cu-P合金的耐蚀性和耐冲刷腐蚀性能.结果表明,Ni-Cu-P合金镀层具有比Ni-P合金镀层更好的热稳定性、耐蚀性和耐冲刷腐蚀性能.
关键词:
化学镀Ni-P
,
化学镀Ni-Cu-P合金
,
耐蚀性
,
冲刷腐蚀
,
热稳定性
施力匀
,
刘定富
,
曾庆雨
,
孔令海
,
沈岳军
电镀与精饰
doi:10.3969/j.issn.1001-3849.2017.05.003
在酸性化学镀镍镀液中分别加入Ce、La、Y、Sm、Sc、Lu和Tm七种稀土元素,对基材进行化学镀镍,探究稀土元素对沉积速率、镀层孔隙率及表面形貌的影响.结果证明,七种稀土元素对沉积速率以及镀层性能影响各不相同.其中,Ce、Y和Lu三种稀土元素在一定质量浓度范围内有加速作用,加入4 mg/L Ce的加速比最大,为18.05％.七种稀土元素对镀层孔隙率均有抑制作用,最低能达到0.32个/cm2.
关键词:
稀土元素
,
沉积速率
,
孔隙率
,
化学镀镍-磷合金